Kobs India is Manufacturer, Stockists & Supplier of premium quality range of ANSI/ASME B16.9 Duplex Buttweld Pipe Nipple, Duplex Steel Nipple & Other Duplex Steel Pipe fittings that are manufactured under the expert guidance of our diligent workforce. we are highly experienced company in ANSI/ASME B16.9 Duplex Steel Buttweld Pipe Nipple & other pipe fittings. Our ANSI/ASME B16.9 Duplex Steel Buttweld Pipe Nipple & Other Fitting products are manufactured using quality material and go through a rigorous quality check at all stages of production to ensure quality. Designed in compliance with international quality standards, these ANSI/ASME B16.9 Butt Welding Pipe Nipples are corrosion resistance, sturdy and durable. We also supply ANSI/ASME B16.9 Duplex Steel Buttweld Pipe Nipple & other pipe fittings Flanges in customized size. Our Product Supply Division offers a broad portfolio of Steel Flanges and ANSI/ASME B16.9 Duplex Steel Buttweld Pipe Nipple. When you place an order with Kobs India , you will receive the products that will stand up in service from people that will stand behind their product.
Kobs India is highly acclaimed & Exporter Presents best offer ever on ANSI/ASME B16.9 Duplex Steel Buttweld Pipe Nipple of different shapes and size with different specifications as per the international standard. We have a wide selection of ANSI/ASME B16.9 Duplex Steel Buttweld Pipe Nipple that has amazing features such as durability, precision and accuracy. We have a team of experienced people who contribute too much to provide the premium quality product at an affordable rate. These pipe nipples are one of the most important need in the process of pipelining in every building. These nipples have got a very good finishing externally as well as internally. We put our best to satisfy each client and keep the best name in the leading companies.
|
Duplex Steel: Grade: 2205 (1.4507) |
| Grade | Common Name | C% | Mn% | Si% | P% | S% | Cr% | Ni% | Mo% | N% |
|---|---|---|---|---|---|---|---|---|---|---|
| 2205 (1.4507) | S31803 | 0.030 | 2.00 | 1.00 | 0.030 | 0.020 | 21.0-23.0 | 4.5-6.5 | 2.5-3.5 | 0.08-0.20 |
| 2205 (1.4507) | S32205 | 0.030 | 2.00 | 1.00 | 0.030 | 0.020 | 22.0-23.0 | 4.5-6.5 | 3.0-3.5 | 0.14-0.20 |
| Tensile strength | 620MPa min | Density | 7,805kg/m3 |
|---|---|---|---|
| Yield strength | 450MPa mi | Elastic modulus | 200GPa |
|
Stainless Steel : Grade: 304 (1.4301), 304L(1.4307), 304H (1.4948), 309 (1.4828), 309S, 310, 310S (1.4845), 316( 1.4401), 316H, 316L( 1.4404 /1.4432) , 317, 317L (1.4438), 321 (1.4541), 321 H(1.4878), 347 (1.4550), 347H (1.4961), 904L (1.4539) Nickel : Grade: Nickel 200, Nickel 201 Super Duplex Steel: Grade: 2507 (UNS S32750), Z100 Inconel : Grade: Inconel 600 (2.4640), Inconel 601 (2.4851), Inconel 625 (2.4856), Inconel 718(2.4668) Titanium : Grade: Gr.1 (3.7025) , Gr.2 (3.7035) , Gr.3(3.7055) , Gr.5(3.7164/65), Gr. 7(3.7235) , Gr. 11 (3.7225) Monel : Grade: Monel 400 ( 2.4360) ( 2.4360), Monel K500 (2.4375), Monel R-405 Hastalloy : Grade: Hastalloy B2, Hastalloy B3, Hastalloy C22, Hastalloy C276, Hastalloy X Incoloy : Grade: Incoloy 800(2.4958), Incoloy 800H, Incoloy 800HT |
The principal methods of hot working are extrusion, drawing, forging and rolling. Rolling is the most extensive employed forming process, though some limitations may apply to the process. Rolling mainly consists of three major sub-categories: flat rolling, shape rolling (with specifically designed roll grooves) and pipe rolling (including piercing). Forging may be sub-categorized as hamming, pressing, etc. .
Forging may be performed under hammers, in mechanical presses and upsetters or by a method known as roll forging. Pressing generally includes the manufacture of forged articles in hydraulic presses. Extrusion usually is performed in hydraulic presses which force the hot steel through a die. Rolling is performed in rolling mills of a variety of types. .
The two principal reasons for perform metal forming at elevated temperatures (hot working) are to reduce the forming loads through the reduction of the resistance of the steel to deformation, and to develop preferred metallurgical structures for strength and ductility of the finish products.
The most appropriate manufacturing method of a product will be decided with consideration of its material, sizes, shape, use, standards and other properties.